• blanking punch life improvement by laser cladding

    جزئیات بیشتر مقاله
    • تاریخ ارائه: 1390/01/01
    • تاریخ انتشار در تی پی بین: 1390/01/01
    • تعداد بازدید: 676
    • تعداد پرسش و پاسخ ها: 0
    • شماره تماس دبیرخانه رویداد: -
      the aisi d2 tool steel samples and punches were laser cladded with the application of various laser pulse shapes, preheating and cryogenic treatment. the samples were subjected to metallographic observations and sliding wear test and the punches were inserted into the stamping tool and subjected to real operation. the results suggest that the laboratory tests by themselves are not decisive for the prediction of refurbishment wear behavior or failure. the claddings made by a and b pulses exhibited solidification cracking and failed in a punch application test, although their wear results were comparable with the others or even better. the c-type claddings could all be employed for punch refurbishment with the advantage of preheating to mitigate the interpass haz cracking. the preheated and cryogenically treated cladding has shown superior edge stability, smooth and ductile wear behavior and moderate interpass cracking.

سوال خود را در مورد این مقاله مطرح نمایید :

با انتخاب دکمه ثبت پرسش، موافقت خود را با قوانین انتشار محتوا در وبسایت تی پی بین اعلام می کنم
مقالات جدیدترین رویدادها